| 品牌 | 台湾奇美 |
| 货号 | PA-777B |
| 用途 | 台湾奇美 |
| 牌号 | PA-777B |
| 型号 | PA-777B |
| 品名 | ABS |
| 特性级别 | 标准级||| |
| 加工级别 | 注塑级|||挤出级|||吹塑级||| |
| 包装规格 | 25公斤/包 |
| 外形尺寸 | 颗粒 |
| 厂家 | 台湾奇美 |
| 用途级别 | 食品级|||汽车部件|||电子电器部件|||照明灯具|||运动器材|||医用级|||家电部件|||电动工具配件||| |
| 是否进口 | 是 |
| 基本信息 | |
|---|---|
| 黄卡编号 |
|
| RoHS 合规性 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.03 | g/cm³ | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (220°C/10.0 kg) | 7.5 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR） (220°C/10.0 kg) | 7.50 | cm³/10min | ISO 1133 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 (R 级) | 112 | ASTM D785 | |
| 球压硬度 (H 358/30) | 91.0 | MPa | ISO 2039-1 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸应力 | |||
| 屈服 | 45.0 | MPa | ISO 527-2/50 |
| 断裂 | 34.0 | MPa | ISO 527-2/50 |
| 3.00 mm 1 | 42.7 | MPa | ASTM D638 |
| 伸长率 | |||
| 断裂, 3.00 mm 2 | 15 | % | ASTM D638 |
| 断裂 | 18 | % | ISO 527-2/50 |
| 弯曲模量 | |||
| 6.00 mm 3 | 2160 | MPa | ASTM D790 |
| -- 4 | 2200 | MPa | ISO 178 |
| 弯曲强度 | |||
| 6.00 mm 5 | 63.7 | MPa | ASTM D790 |
| -- 6 | 70.0 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | 20 | kJ/m² | ISO 179 |
| 悬壁梁缺口冲击强度 | |||
| 23°C, 3.00 mm | 230 | J/m | ASTM D256 |
| 23°C, 6.00 mm | 200 | J/m | ASTM D256 |
| -- | 19 | kJ/m² | ISO 180/1A |
ABS台湾奇美 PA-777B详细说明
ABS台湾奇美 PA-777B原料物性描述:
ABS 树脂是丙烯腈-丁二烯-苯乙烯共聚物，英文名Acrylonitrile-butadine-styrene（简称ABS），是大宗通用树脂，经过改性（加添加剂或合金等方法）提高性能后的ABS属工程塑料，ABS合金产量大，种类多，应用广，是主要改性塑料。
ABS为浅黄色粒状或珠状不透明树脂，无毒、无味、吸水率低，具有良好的综合物理机械性能，如优良的电性能、耐磨性，尺寸稳定性、耐化学性和表面光泽等，且易于加工成型。缺点是耐候性，耐热性差，且易燃。
ABS具有良好的机械强度、韧性和阻燃性，用于建材，汽车和电子工业，如做电视机、办公自动化设备外壳和电话机。ABS/PC合金中PC贡献耐热性、韧性、冲击强度、强度阻燃性、ABS优点为良好加工性、表观质量和低密度，以汽车工业零部件为应用重点。
ABS台湾奇美 PA-727俗称不碎胶，属通用塑料。
优点：坚硬、易押出、易染色、难燃、耐冲击、表面性佳。
用途：把手、外壳、行李箱、冰箱衬垫、电视机壳、复印机壳、电话机壳、化妆品盒、灯座、玩具、鞋跟、家电制品、齿轮、汽车配件、挡泥板、扶手、冰箱内衬、叶片、轴承、把手、管道、接头、仪表壳、仪表板、盘、安全帽等。
分类：吹塑成型ABS、挤出成型ABS、玻纤增强ABS、阻燃增强ABS、耐环境开裂ABS、超高耐热ABS、冰箱薄板级ABS、阻燃5V级ABS、 型ABS、耐药性ABS、防静电ABS、耐磨高润滑ABS、耐候性ABS、阻燃耐候抗"UV"ABS、ABS粉料、抗紫外线ABS。
台湾奇美ABS PA-737 食品级
台湾奇美ABS PA-758 高透明性
台湾奇美ABS PA-765A 防火 高流动
台湾奇美ABS PA-777B PA-777D PA-777E 耐热
台湾奇美ABS PA-718 高光泽、高硬度 钢琴拷漆
美国GE ABS FR15U 防火 抗紫外线
美国GE ABS MG37EP 耐热
供应ABS台湾奇美PA-727 电镀
供应ABS台湾奇美PA-737 食品级 高流动
供应ABS台湾奇美PA-758 高透明性
供应ABS台湾奇美PA-765A 防火 高流动
供应ABS台湾奇美PA-777B 耐热
供应ABS台湾奇美PA-777D 耐热级
供应ABS台湾奇美PA-777E 耐热级
供应ABS基础创新（美国GE）FR15U 防火 抗紫外线
供应ABS韩国锦湖HFA705 防火 抗紫外线
供应ABS台湾奇美PA-764B 防火 抗紫外线
供应ABS日本旭化成 SX200
ABS沙伯基础MG38F 医疗级食品级
ABS沙伯基础 HP30 医疗级食品级
食品级ABS韩国锦湖ER875 医疗级食品级
POLYLAC® PA-777B
Acrylonitrile Butadiene Styrene
CHI MEI CORPORATION
Product Description:
POLYLAC® PA-777B is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive.
Characteristics include:
Flame Rated
RoHS Compliant
Heat Resistant
Impact Resistant
| General | |
| Material Status |
|
| Literature 1 |
|
| UL Yellow Card 2 |
|
| Search for UL Yellow Card |
|
| Availability | Africa & Middle EastAsia PacificEuropeLatin AmericaNorth America |
| Features | High Impact ResistanceMedium Heat Resistance |
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
| Density / Specific Gravity | | | |
| -- 3 | 1.03 | g/cm3 | ASTM D792 |
| 23°C | 1.03 | g/cm3 | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 7.5 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 8.5 | cm3/10min | ISO 1133 |
| Molding Shrinkage | 0.30 to 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
| Rockwell Hardness (R-Scale) | 112 | | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Strength | | | |
| Yield 4 | 43.0 | MPa | ASTM D638 |
| Yield | 44.0 | MPa | ISO 527-2/50 |
| Break | 34.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | | | |
| Break 4 | 15 | % | ASTM D638 |
| Break | 40 | % | ISO 527-2/50 |
| Flexural Modulus | | | |
| -- 5 | 2140 | MPa | ASTM D790 |
| -- 6 | 2200 | MPa | ISO 178 |
| Flexural Strength | | | |
| -- 5 | 63.4 | MPa | ASTM D790 |
| -- 6 | 67.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
| Charpy Notched Impact Strength | | | ISO 179 |
| -30°C | 11 | kJ/m2 | |
| 23°C | 22 | kJ/m2 | |
| Notched Izod Impact | | | |
| 23°C, 3.20 mm | 230 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 200 | J/m | ASTM D256 |
| -30°C | 11 | kJ/m2 | ISO 180/1A |
| 23°C | 21 | kJ/m2 | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
| Deflection Temperature Under Load | | | |
| 1.8 MPa, Unannealed | 97.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 86.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 107 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 106 | °C | ISO 75-2/A |
| Vicat Softening Temperature | | | |
| -- | 115 | °C | ASTM D1525 7 |
| -- | 106 | °C | ISO 306/B50 |
| -- | 114 | °C | ISO 306/A50 |
| CLTE - Flow | 8.4E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | | Test Method |
| Flame Rating (1.5 mm) | HB | | UL 94 |
| Injection | Nominal Value | Unit | |
| Drying Temperature | 90 to 95 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Mold Temperature | 30 to 70 | °C | |
| Injection Pressure | 4.90 to 6.86 | MPa | |
| Holding Pressure | 3.92 to 5.88 | MPa | |
| Back Pressure | 0.490 to 1.47 | MPa | |
| Notes |