NORYL™ Resin N225X - Americas
聚苯醚 + PS
SABIC
Product Description:
NORYL™ N225X resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of 5VA at 3mm and V0 at 1.5mm along with a UL746C Outdoor Suitability rating of F1. NORYL N225X resin offers good dielectric strength and strong electrical performance in addition to low moisture absorption and dimensional stability, This material is an excellent candidate for both indoor and outdoor electrical applications.
| 总览 | |
材料状态 |
|
UL 黄卡 1 |
|
搜索 UL 黄卡 |
|
供货地区 | 北美洲拉丁美洲 |
用途 | 电气/电子应用领域电器用具电子显示器建筑应用领域汽车的发动机罩下的零件 |
多点数据 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
密度 / 比重 | 1.11 | g/cm3 | ASTM D792 |
收缩率 | 内部方法 | ||
垂直 : 3.20 mm | 0.50 到 0.70 | % | |
流动 : 3.20 mm | 0.50 到 0.70 | % | |
室外适用性 | f1 | UL 746C |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
抗张强度 2 | ASTM D638 | ||
屈服 | 66.0 | MPa | |
断裂 | 49.0 | MPa | |
伸长率 2 | ASTM D638 | ||
屈服 | 8.0 | % | |
断裂 | 17 | % | |
弯曲模量 3 (100 mm 跨距) | 2490 | MPa | ASTM D790 |
弯曲强度 3 (屈服, 100 mm 跨距) | 99.0 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
悬壁梁缺口冲击强度 | ASTM D256 | ||
-30°C | 96 | J/m | |
23°C | 190 | J/m | |
反向缺口冲击 (3.20 mm) | 890 | J/m | ASTM D256 |
装有测量仪表的落镖冲击 | ASTM D3763 | ||
-30°C, Energy at Peak | 11.0 | J | |
23°C, Energy at Peak | 39.0 | J |
| 热性能 | 额定值 | 单位制 | 测试方法 |
载荷下热变形温度 | ASTM D648 | ||
0.45 MPa, 未退火, 6.40 mm | 109 | °C | |
1.8 MPa, 未退火, 6.40 mm | 99.0 | °C | |
维卡软化温度 | 128 | °C | ASTM D1525 4 |
RTI Elec 5 | 95.0 | °C | UL 746 |
RTI Imp 5 | 80.0 | °C | UL 746 |
RTI 5 | 95.0 | °C | UL 746 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
表面电阻率 | > 1.0E+14 | ohms | ASTM D257 |
体积电阻率 | 2.8E+16 | ohms·cm | ASTM D257 |
介电强度 (3.20 mm, in Oil) | 16 | kV/mm | ASTM D149 |
介电常数 | ASTM D150 | ||
60 Hz | 2.69 | ||
50 kHz | 2.69 | ||
1 MHz | 2.55 | ||
耗散因数 | ASTM D150 | ||
50 Hz | 0.010 | ||
60 Hz | 0.010 | ||
1 MHz | 7.0E-3 | ||
耐电弧性 6 | PLC 6 | ASTM D495 | |
相比耐漏电起痕指数(CTI) | PLC 1 | UL 746 | |
高电弧燃烧指数(HAI) (> 1.5 mm) | PLC 0 | UL 746 | |
高电压电弧起痕速率 (HVTR) | PLC 4 | UL 746 | |
热丝引燃 (HWI) | UL 746 | ||
> 1.5 mm | PLC 1 | ||
> 6.0 mm | PLC 0 | ||
| 可燃性 | 额定值 | 单位制 | 测试方法 |
UL 阻燃等级 | UL 94 | ||
> 0.40 mm | HB | ||
> 1.5 mm | V-0 | ||
> 3.0 mm | 5VA | ||
Radiant Panel Listing | TRUE | UL Unspecified |
| 注射 | 额定值 | 单位制 | |
干燥温度 | 95 到 100 | °C | |
干燥时间 | 3.0 到 4.0 | hr | |
建议的*水分含量 | 0.020 | % | |
建议注射量 | 30 到 70 | % | |
料筒后部温度 | 225 到 275 | °C | |
料筒中部温度 | 240 到 280 | °C | |
料筒前部温度 | 250 到 290 | °C | |
射嘴温度 | 260 到 290 | °C | |
加工（熔体）温度 | 260 到 290 | °C | |
模具温度 | 70 到 95 | °C | |
背压 | 0.300 到 0.700 | MPa | |
螺杆转速 | 20 到 100 | rpm | |
排气孔深度 | 0.038 到 0.051 | mm |