NORYL™ Resin PX9406P - Asia
Polyphenylene Ether + PS
SABIC
Product Description:
NORYL™ PX9406P resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of 5VA at 2.5mm and V0 at 0.75mm. NORYL PX9406P is VDE certified IEC60335 and offers strong electrical performance at thin wall, high heat resistance, Low Warpage, low moisture absorption, and dimensional stability. This material is an excellent candidate for unattended appliance applications such as printed circuit board (PCB) holders, terminal blocks + connectors, circuit protection / relay / switches, motor end caps, control box / panels, and battery charger / fuse holders where VDE IEC60335 is required.
Material Status |
|
Availability |
|
Uses | AppliancesConstruction ApplicationsElectrical/Electronic ApplicationsElectronic DisplaysLighting Applications |
Also Available In | EuropeLatin AmericaNorth America |
| Physical | Nominal Value | Unit | Test Method |
Density / Specific Gravity | 1.10 | g/cm3 | ASTM D792, ISO 1183 |
Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 3.9 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 10 | cm3/10min | ISO 1133 |
Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
Water Absorption (24 hr) | 0.070 | % | ASTM D570 |
Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Stress | |||
Yield | 63.0 | MPa | Internal Method |
Yield | 73.0 | MPa | ISO 527-2/50 |
Tensile Strain | |||
Break | 8.5 | % | Internal Method |
Break | 8.0 | % | ISO 527-2/50 |
Flexural Modulus | |||
-- | 2350 | MPa | ASTM D790 |
-- 2 | 2500 | MPa | ISO 178 |
Flexural Strength | |||
-- | 99.0 | MPa | ASTM D790 |
-- 2, 3 | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength 4 (23°C) | 11 | kJ/m2 | ISO 179/1eA |
Charpy Unnotched Impact Strength 4 (-30°C) | 9.0 | kJ/m2 | ISO 179/1eU |
Notched Izod Impact | |||
23°C | 140 | J/m | ASTM D256 |
-40°C 5 | 8.0 | kJ/m2 | ISO 180/1A |
-30°C 5 | 6.0 | kJ/m2 | ISO 180/1A |
-20°C 5 | 9.0 | kJ/m2 | ISO 180/1A |
-10°C 5 | 10 | kJ/m2 | ISO 180/1A |
0°C 5 | 11 | kJ/m2 | ISO 180/1A |
23°C 5 | 10 | kJ/m2 | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed, 6.40 mm | 136 | °C | ASTM D648 |
1.8 MPa, Unannealed, 6.40 mm | 122 | °C | ASTM D648 |
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 5 | 117 | °C | ISO 75-2/Af |
Vicat Softening Temperature | |||
-- | 140 | °C | ISO 306/B120 |
-- | 150 | °C | ISO 306/A120 |
Ball Pressure Test 6 (125°C) | Pass | IEC 60695-10-2 | |
CLTE | |||
Flow : -30 to 30°C | 7.0E-5 | cm/cm/°C | TMA |
Flow : -40 to 40°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
Transverse : -40°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
RTI Elec 7 | 110 | °C | UL 746 |
RTI Imp 7 | 105 | °C | UL 746 |
RTI Str 7 | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
Dielectric Constant | ASTM D150 | ||
60 Hz | 2.80 | ||
50 kHz | 2.80 | ||
Arc Resistance 8 | PLC 6 | ASTM D495 | |
Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
High Amp Arc Ignition (HAI) (> 0.75 mm) | PLC 0 | UL 746 | |
High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
Hot-wire Ignition (HWI) (> 0.75 mm) | PLC 0 | UL 746 | |
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating | UL 94 | ||
> 0.40 mm | V-2 | ||
> 0.75 mm | V-0 | ||
> 2.0 mm | 5VB | ||
> 2.5 mm | 5VA | ||
Glow Wire Flammability Index | IEC 60695-2-12 | ||
0.75 mm | 960 | °C | |
1.0 mm | 960 | °C | |
1.5 mm | 960 | °C | |
3.0 mm | 960 | °C | |
Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
0.75 mm | 750 | °C | |
1.0 mm | 775 | °C | |
1.5 mm | 775 | °C | |
3.0 mm | 775 | °C |
| Fill Analysis | Nominal Value | Unit | Test Method |
Melt Viscosity (280°C, 1500 sec^-1) | 278 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
Drying Temperature | 105 to 110 | °C | |
Drying Time | 3.0 to 4.0 | hr | |
Suggested Max Moisture | 0.020 | % | |
Suggested Shot Size | 30 to 70 | % | |
Rear Temperature | 245 to 295 | °C | |
Middle Temperature | 255 to 300 | °C | |
Front Temperature | 265 to 305 | °C | |
Nozzle Temperature | 275 to 305 | °C | |
Processing (Melt) Temp | 275 to 305 | °C | |
Mold Temperature | 70 to 100 | °C | |
Back Pressure | 0.300 to 0.700 | MPa | |
Screw Speed | 20 to 100 | rpm | |
Vent Depth | 0.038 to 0.051 | mm |