| 特性级别 | 增韧级||| |
| 牌号 | GFN1 |
| 加工级别 | 注塑级||| |
| 品名 | NORYL Resin GFN1 - Americas |
| 厂家(产地) | 基础创新塑料美国(美国液氮) |
| 用途级别 | 电子电器部件|||家电部件|||电动工具配件||| |
基础创新塑料PP0 GFN1 添加10%玻璃纤维 用于从安培表零件到泵外壳
Tensile Modulus | |||
-- 2 | 4350 | MPa | ASTM D638 |
-- | 4400 | MPa | ISO 527-2/1 |
Tensile Strength | |||
Break 3 | 63.0 | MPa | ASTM D638 |
Break | 64.0 | MPa | ISO 527-2 |
Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
Flexural Modulus | |||
50.0 mm Span 4 | 3840 | MPa | ASTM D790 |
100 mm Span 5 | 3580 | MPa | ASTM D790 |
-- | 4160 | MPa | ISO 178 |
Flexural Stress | |||
-- | 122 | MPa | ISO 178 |
Yield, 50.0 mm Span 4 | 116 | MPa | ASTM D790 |
Yield, 100 mm Span 5 | 107 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/2C | ||
-30°C | 9.0 | kJ/m2 | |
23°C | 11 | kJ/m2 | |
Charpy Unnotched Impact Strength 6 | ISO 179/1eU | ||
-30°C | 33 | kJ/m2 | |
23°C | 34 | kJ/m2 | |
Notched Izod Impact | |||
-30°C | 100 | J/m | ASTM D256 |
23°C | 120 | J/m | ASTM D256 |
-30°C 7 | 9.0 | kJ/m2 | ISO 180/1A |
23°C 7 | 10 | kJ/m2 | ISO 180/1A |
Unnotched Izod Impact | |||
23°C | 450 | J/m | ASTM D4812 |
-30°C 7 | 25 | kJ/m2 | ISO 180/1U |
23°C 7 | 27 | kJ/m2 | ISO 180/1U |
Instrumented Dart Impact (23°C, Total Energy) | 21.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed, 3.20 mm | 131 | °C | ASTM D648 |
0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 8 | 132 | °C | ISO 75-2/Be |
1.8 MPa, Unannealed, 3.20 mm | 122 | °C | ASTM D648 |
1.8 MPa, Unannealed, 6.40 mm | 125 | °C | ASTM D648 |
1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 8 | 124 | °C | ISO 75-2/Ae |
Vicat Softening Temperature | |||
-- | 131 | °C | ISO 306/B50 |
-- | 134 | °C | ISO 306/B120 |
CLTE | ASTM E831 | ||
Flow : -40 to 40°C | 5.1E-5 | cm/cm/°C | |
Transverse : -40 to 40°C | 7.1E-5 | cm/cm/°C | |
RTI Elec | 90.0 | °C | UL 746 |
RTI Imp | 90.0 | °C | UL 746 |
RTI Str | 90.0 | °C | UL 746 |