日本三井化学PA6T A335物性表
Availability |
North America
|
Filler / Reinforcement |
Glass Fiber, 35% Filler by Weight
|
Forms |
Pellets
|
PHYSICAL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Density / Specific Gravity |
1.48
|
--
|
g/cm3
|
ASTM D792 |
Molding Shrinkage | ASTM D955 | |||
Flow : 2.00 mm |
0.30
|
--
|
%
|
|
Across Flow : 2.00 mm |
0.60
|
--
|
%
|
|
Water Absorption | ASTM D570 | |||
24 hr, 23°C |
0.30
|
--
|
%
|
|
24 hr, 100°C |
1.8
|
--
|
%
|
MECHANICAL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Strength |
240
|
220
|
MPa
|
ASTM D638 |
Tensile Elongation (Break) |
3.0
|
3.0
|
%
|
ASTM D638 |
Flexural Modulus |
12000
|
11000
|
MPa
|
ASTM D790 |
Flexural Strength |
360
|
320
|
MPa
|
ASTM D790 |
IMPACT |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Notched Izod Impact |
130
|
150
|
J/m
|
ASTM D256 |
HARDNESS |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Rockwell Hardness (M-Scale) |
110
|
--
|
|
ASTM D785 |
THERMAL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Deflection Temperature Under Load (1.8 MPa, Unannealed) |
310
|
--
|
°C
|
ASTM D648 |
Glass Transition Temperature |
125
|
--
|
°C
|
DSC |
Melting Temperature |
320
|
--
|
°C
|
|
CLTE | ASTM D696 | |||
Flow |
2.0E-5
|
--
|
cm/cm/°C
|
|
Transverse |
4.5E-5
|
--
|
cm/cm/°C
|
ELECTRICAL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Volume Resistivity |
1.0E+16
|
--
|
ohms·cm
|
ASTM D257 |
Dielectric Strength |
27
|
--
|
kV/mm
|
ASTM D149 |
Dielectric Constant (1 MHz) |
4.50
|
--
|
|
ASTM D150 |
Dissipation Factor (1 MHz) |
0.018
|
--
|
|
ASTM D150 |
FLAMMABILITY |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Flame Rating |
HB
|
--
|
|
UL 94 |
INJECTION |
Dry
|
Unit
|
|
Drying Temperature |
110
|
°C
|
|
Drying Time |
2.0 to 6.0
|
hr
|
|
Hopper Temperature |
50 to 90
|
°C
|
|
Rear Temperature |
315 to 330
|
°C
|
|
Middle Temperature |
320 to 335
|
°C
|
|
Front Temperature |
325 to 340
|
°C
|
|
Nozzle Temperature |
325 to 340
|
°C
|
|
Mold Temperature |
90 to 140
|
°C
|
|
Injection Rate |
Moderate
|
|
|
Screw Speed |
150
|
rpm
|
|
INJECTION NOTES | |||
Injection Pressure: Medium Pressure
|