| 品牌 | 日本三井化学 |
| 货号 | 012 |
| 用途 | 汽车零件 |
| 牌号 | ARLEN |
| 型号 | 日本三井化学 |
| 品名 | PA6T |
| 外形尺寸 | PELLETS |
| 生产企业 | 广裕塑胶 |
| 是否进口 | 是 |
日本三井化学PA6T A315 PELLETS
| Availability |
North America
|
| Filler / Reinforcement |
Glass Fiber, 15% Filler by Weight
|
| Forms |
Pellets
|
| PHYSICAL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Density / Specific Gravity |
1.30
|
--
|
g/cm3
|
ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow : 2.00 mm |
0.50
|
--
|
%
|
|
| Across Flow : 2.00 mm |
0.60
|
--
|
%
|
|
| Water Absorption | ASTM D570 | |||
| 24 hr, 23°C |
0.40
|
--
|
%
|
|
| 24 hr, 100°C |
2.5
|
--
|
%
|
| MECHANICAL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Tensile Strength |
120
|
110
|
MPa
|
ASTM D638 |
| Tensile Elongation (Break) |
3.0
|
3.0
|
%
|
ASTM D638 |
| Flexural Modulus |
6000
|
5500
|
MPa
|
ASTM D790 |
| Flexural Strength |
190
|
170
|
MPa
|
ASTM D790 |
| IMPACT |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Notched Izod Impact |
50
|
70
|
J/m
|
ASTM D256 |
| HARDNESS |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Rockwell Hardness (M-Scale) |
105
|
--
|
|
ASTM D785 |
| THERMAL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) |
290
|
--
|
°C
|
ASTM D648 |
| Glass Transition Temperature |
125
|
--
|
°C
|
DSC |
| Melting Temperature |
320
|
--
|
°C
|
|
| CLTE | ASTM D696 | |||
| Flow |
3.4E-5
|
--
|
cm/cm/°C
|
|
| Transverse |
5.5E-5
|
--
|
cm/cm/°C
|
| ELECTRICAL |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Volume Resistivity |
1.0E+16
|
--
|
ohms·cm
|
ASTM D257 |
| Dielectric Strength |
25
|
--
|
kV/mm
|
ASTM D149 |
| Dielectric Constant (1 MHz) |
4.20
|
--
|
|
ASTM D150 |
| Dissipation Factor (1 MHz) |
0.020
|
--
|
|
ASTM D150 |
| FLAMMABILITY |
Dry
|
Conditioned
|
Unit
|
Test Method
|
| Flame Rating |
HB
|
--
|
|
UL 94 |
| INJECTION |
Dry
|
Unit
|
|
| Drying Temperature |
110
|
°C
|
|
| Drying Time |
2.0 to 6.0
|
hr
|
|
| Hopper Temperature |
50 to 90
|
°C
|
|
| Rear Temperature |
315 to 330
|
°C
|
|
| Middle Temperature |
320 to 335
|
°C
|
|
| Front Temperature |
325 to 340
|
°C
|
|
| Nozzle Temperature |
325 to 340
|
°C
|
|
| Mold Temperature |
90 to 140
|
°C
|
|
| Injection Rate |
Moderate
|
|
|
| Screw Speed |
150
|
rpm
|
|
| INJECTION NOTES | |||
|
Injection Pressure: Medium Pressure
|
|||
| NOTES |
| 1These links provide you with access to supplier literature. We work hard to keep them up to date; however you may find the most current literature from the supplier. |
| 2Typical properties: these are not to be construed as specifications. |