| 品牌 | 日本住友 |
| 货号 | GY-E5008L |
| 用途 | 隔热件 |
| 牌号 | SUMIKASUPER |
| 型号 | E6006L |
| 品名 | LCP |
| 外形尺寸 | 2*3 |
| 生产企业 | 广裕公司 |
| 是否进口 | 是 |
日本住友 LCP E6006L物性表
| Molding Shrinkage | Internal Method | ||
| Flow : 3.00 mm |
0.19
|
%
|
|
| Across Flow : 3.00 mm |
0.74
|
%
|
|
| Water Absorption (24 hr, 23°C) |
0.020
|
%
|
ASTM D570 |
| MECHANICAL |
Nominal Value
|
Unit
|
Test Method
|
| Tensile Modulus |
11500
|
MPa
|
ISO 527-1 |
| Tensile Strength | |||
| -- |
164
|
MPa
|
ASTM D638 |
| -- |
115
|
MPa
|
ISO 527-2 |
| Tensile Elongation | |||
| Break |
5.0
|
%
|
ASTM D638 |
| Break |
1.5
|
%
|
ISO 527-2 |
| Flexural Modulus | |||
| -- |
11300
|
MPa
|
ASTM D790 |
| -- |
13300
|
MPa
|
ISO 178 |
| Flexural Strength | |||
| -- |
153
|
MPa
|
ASTM D790 |
| -- |
184
|
MPa
|
ISO 178 |
| Poisson's Ratio |
0.49
|
|
ISO 527-1 |
| IMPACT |
Nominal Value
|
Unit
|
Test Method
|
| Charpy Unnotched Impact Strength |
44
|
kJ/m2
|
ISO 179/1eU |
| Unnotched Izod Impact | |||
| -- |
360
|
J/m
|
ASTM D256 |
| -- |
32
|
kJ/m2
|
ISO 180/1U |
| HARDNESS |
Nominal Value
|
Unit
|
Test Method
|
| Rockwell Hardness (R-Scale) |
113
|
|
ASTM D785 |
| THERMAL |
Nominal Value
|
Unit
|
Test Method
|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed |
315
|
°C
|
ASTM D648 |
| 0.45 MPa, Unannealed |
320
|
°C
|
ISO 75-2/B |
| 1.8 MPa, Unannealed |
284
|
°C
|
ASTM D648 |
| 1.8 MPa, Unannealed |
228
|
°C
|
ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow : 50 to 150°C |
2.0E-5
|
cm/cm/°C
|
|
| Transverse : 50 to 150°C |
8.9E-5
|
cm/cm/°C
|
| ELECTRICAL |
Nominal Value
|
Unit
|
Test Method
|
| Volume Resistivity |
1.0E+13
|
ohms·cm
|
IEC 60093 |
| Electric Strength (1.00 mm) |
48
|
kV/mm
|
IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 1 MHz |
3.70
|
|
|
| 1.00 GHz |
3.50
|
|
|
| 10.0 GHz |
3.60
|
|
|
| Dissipation Factor | IEC 60250 | ||
| 1 MHz |
0.034
|
|
|
| 1.00 GHz |
5.0E-3
|
|
|
| 10.0 GHz |
5.0E-3
|
|
|
| Arc Resistance |
130
|
sec
|
ASTM D495 |
| Comparative Tracking Index |
175
|
V
|
IEC 60112 |
| FLAMMABILITY |
Nominal Value
|
Unit
|
Test Method
|
| Flammability Classification |
V-0
|
|
IEC 60695-11-10, -20 |
| INJECTION |
Nominal Value
|
Unit
|
|
| Drying Temperature |
120 to 140
|
°C
|
|
| Drying Time |
4.0 to 24
|
hr
|
|
| Rear Temperature |
280 to 320
|
°C
|
|
| Middle Temperature |
320 to 340
|
°C
|
|
| Front Temperature |
340 to 370
|
°C
|
|
| Nozzle Temperature |
340 to 370
|
°C
|
|
| Processing (Melt) Temp |
340 to 370
|
°C
|
|
| Mold Temperature |
60 to 160
|
°C
|
|
| Injection Pressure |
80.0 to 160
|
MPa
|
|
| Holding Pressure |
10.0 to 80.0
|
MPa
|
|
| Back Pressure |
0.500 to 5.00
|
MPa
|
|
| Screw Speed |
50 to 350
|
rpm
|