德国巴斯夫PA66 A3WG5物性表:
Physical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Density / Specific Gravity
|
1.32
|
--
|
g/cm3
|
ASTM D792, ISO 1183 |
Melt Volume-Flow Rate (MVR) (275°C/5.0 kg)
|
50
|
--
|
cm3/10min
|
ISO 1133 |
Molding Shrinkage - Flow (3.18 mm)
|
0.30
|
--
|
%
|
|
Water Absorption
|
||||
Saturation
|
6.0
|
--
|
%
|
ASTM D570 |
Saturation, 23°C
|
6.0
|
--
|
%
|
ISO 62 |
Equilibrium, 50% RH
|
1.9
|
--
|
%
|
ASTM D570 |
Equilibrium, 23°C, 50% RH
|
1.9
|
--
|
%
|
ISO 62 |
Mechanical |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Tensile Modulus (23°C)
|
8600
|
6500
|
MPa
|
ISO 527-1 |
Tensile Strength
|
||||
Break, 23°C
|
169
|
118
|
MPa
|
ASTM D638 |
Break, 23°C
|
180
|
120
|
MPa
|
ISO 527-2 |
Tensile Elongation
|
||||
Break, 23°C
|
2.8
|
5.0
|
%
|
ASTM D638 |
Break, 23°C
|
2.8
|
6.0
|
%
|
ISO 527-2 |
Flexural Modulus
|
||||
23°C
|
7720
|
5380
|
MPa
|
ASTM D790 |
23°C
|
7600
|
--
|
MPa
|
ISO 178 |
Impact |
Dry
|
Conditioned
|
Unit
|
Test Method
|
Charpy Notched Impact Strength
|
ISO 179 | |||
-30°C
|
9.0
|
--
|
kJ/m2
|
|
23°C
|
10
|
20
|
kJ/m2
|
|
Charpy Unnotched Impact Strength
|
ISO 179 | |||
-30°C
|
55
|
--
|
kJ/m2
|
|
23°C
|
60
|
90
|
kJ/m2
|
|
Notched Izod Impact
|
||||
-40°C
|
69
|
--
|
J/m
|
ASTM D256 |
23°C
|
80
|
--
|
J/m
|
ASTM D256 |
23°C
|
9.5
|
--
|
kJ/m2
|
ISO 180 |