德国巴斯夫PA66 A3W 热稳定 高流动性 耐热老化：
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
1.14
|
g/cm3
|
ASTM D792, ISO 1183 |
|
Water Absorption
|
|||
|
Saturation
|
8.5
|
%
|
ASTM D570 |
|
Saturation, 23°C
|
8.5
|
%
|
ISO 62 |
|
Equilibrium, 50% RH
|
2.8
|
%
|
ASTM D570 |
|
Equilibrium, 23°C, 50% RH
|
2.8
|
%
|
ISO 62 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus (23°C)
|
3300
|
MPa
|
ISO 527-1 |
|
Tensile Strength
|
|||
|
Yield, 23°C
|
85.0
|
MPa
|
ASTM D638 |
|
Yield, 23°C
|
88.0
|
MPa
|
ISO 527-2 |
|
Tensile Elongation
|
|||
|
Yield, 23°C
|
4.5
|
%
|
ASTM D638 |
|
Yield, 23°C
|
4.7
|
%
|
ISO 527-2 |
|
Flexural Modulus (23°C)
|
3100
|
MPa
|
ISO 178 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
ISO 179 | ||
|
-30°C
|
3.0
|
kJ/m2
|
|
|
23°C
|
4.6
|
kJ/m2
|
|
|
Notched Izod Impact
|
|||
|
-40°C
|
48
|
J/m
|
ASTM D256 |
|
23°C
|
53
|
J/m
|
ASTM D256 |
|
-40°C
|
4.0
|
kJ/m2
|
ISO 180 |
|
23°C
|
4.5
|
kJ/m2
|
ISO 180 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
|||
|
0.45 MPa, Unannealed
|
210
|
°C
|
ISO 75-2/B |
|
1.8 MPa, Unannealed
|
75.0
|
°C
|
ISO 75-2/A |
|
Peak Melting Temperature
|
260
|
°C
|
ASTM D3418, ISO 3146 |
|
RTI Elec
|
UL 746B | ||
|
0.75 mm
|
130
|
°C
|
|
|
1.5 mm
|
130
|
°C
|
|
|
3.0 mm
|
130
|
°C
|
|
|
6.0 mm
|
130
|
°C
|
|
|
RTI Imp
|
UL 746B | ||
|
0.75 mm
|
105
|
°C
|
|
|
1.5 mm
|
105
|
°C
|
|
|
3.0 mm
|
105
|
°C
|
|
|
6.0 mm
|
105
|
°C
|
|
|
RTI Str
|
UL 746B | ||
|
0.75 mm
|
105
|
°C
|
|
|
1.5 mm
|
105
|
°C
|
|
|
3.0 mm
|
110
|
°C
|
|
|
6.0 mm
|
110
|
°C
|