全国咨询热线：13431131945
|
| 品牌 | 基础创新塑料 |
| 货号 | C2950HF |
| 用途 | 注塑级 |
| 牌号 | C2950HF |
| 型号 | C2950HF |
| 品名 | PC合金料 |
| 外形尺寸 | 颗粒 |
| 生产企业 | 基础创新塑料 |
| 是否进口 | 是 |
基础创新塑料()C2950HF
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Density / Specific Gravity
|
1.18
|
g/cm3
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (260°C/2.16 kg)
|
22
|
g/10 min
|
ASTM D1238 |
|
Molding Shrinkage
|
Internal Method | ||
|
Across Flow : 3.20 mm
|
0.40 to 0.60
|
%
|
|
|
Flow : 3.20 mm
|
0.40 to 0.60
|
%
|
|
|
Water Absorption
|
ASTM D570 | ||
|
24 hr, 23°C
|
0.10
|
%
|
|
|
Saturation, 23°C
|
0.40
|
%
|
|
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness (R-Scale)
|
121
|
|
ASTM D785 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength 2 (Yield)
|
64.0
|
MPa
|
ASTM D638 |
|
Tensile Elongation 2
|
ASTM D638 | ||
|
Yield
|
5.0
|
%
|
|
|
Break
|
40
|
%
|
|
|
Flexural Modulus 3 (100 mm Span)
|
2580
|
MPa
|
ASTM D790 |
|
Flexural Strength 3 (Yield, 100 mm Span)
|
96.0
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact (23°C)
|
450
|
J/m
|
ASTM D256 |
|
Instrumented Dart Impact (23°C, Energy at Peak)
|
54.0
|
J
|
ASTM D3763 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
ASTM D648 | ||
|
0.45 MPa, Unannealed, 6.40 mm
|
101
|
°C
|
|
|
1.8 MPa, Unannealed, 3.20 mm
|
87.0
|
°C
|
|
|
1.8 MPa, Unannealed, 6.40 mm
|
95.0
|
°C
|
|
|
Vicat Softening Temperature
|
112
|
°C
|
ASTM D1525 4 |
|
CLTE
|
ASTM D696 | ||
|
Flow : -30 to 30°C
|
7.2E-5
|
cm/cm/°C
|
|
|
Transverse : -30 to 30°C
|
7.2E-5
|
cm/cm/°C
|
|
|
Thermal Conductivity
|
0.20
|
W/m/K
|
ASTM C177 |
|
RTI Elec
|
85.0
|
°C
|
UL 746 |
|
RTI Imp
|
85.0
|
°C
|
UL 746 |
|
RTI Str
|
85.0
|
°C
|
UL 746 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Surface Resistivity
|
> 1.0E+16
|
ohms
|
ASTM D257 |
|
Volume Resistivity
|
1.6E+17
|
ohms·cm
|
ASTM D257 |
|
Dielectric Strength (3.20 mm, in Oil)
|
24
|
kV/mm
|
ASTM D149 |
|
Dielectric Constant
|
ASTM D150 | ||
|
60 Hz
|
2.80
|
|
|
|
50 kHz
|
2.80
|
|
|
|
1 MHz
|
2.70
|
|
|
|
Dissipation Factor
|
ASTM D150 | ||
|
50 Hz
|
5.2E-3
|
|
|
|
60 Hz
|
5.2E-3
|
|
|
|
1 MHz
|
7.1E-3
|
|
|
|
Arc Resistance 5
|
PLC 6
|
|
ASTM D495 |
|
Comparative Tracking Index (CTI)
|
PLC 2
|
|
UL 746 |
|
High Amp Arc Ignition (HAI) 6
|
PLC 0
|
|
UL 746 |
|
High Voltage Arc Tracking Rate (HVTR)
|
PLC 3
|
|
UL 746 |
|
Hot-wire Ignition (HWI)
|
PLC 2
|
|
UL 746 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
0.76 mm
|
V-2
|
|
|
|
1.5 mm
|
V-0
|
|
|
|
2.5 mm
|
5VB
|
|
|
|
3.4 mm
|
5VA
|
|
|
|
Oxygen Index
|
30
|
%
|
ASTM D2863 |
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
80 to 90
|
°C
|
|
|
Drying Time
|
3.0 to 4.0
|
hr
|
|
|
Suggested Max Moisture
|
0.040
|
%
|
|
|
Suggested Shot Size
|
30 to 80
|
%
|
|
|
Rear Temperature
|
220 to 255
|
°C
|
|
|
Middle Temperature
|
220 to 265
|
°C
|
|
|
Front Temperature
|
245 to 275
|
°C
|
|
|
Nozzle Temperature
|
245 to 275
|
°C
|
|
|
Processing (Melt) Temp
|
245 to 275
|
°C
|
|
|
Mold Temperature
|
60 to 80
|
°C
|
|
|
Back Pressure
|
0.300 to 0.700
|
MPa
|
PC/ABS在加工产品时，不影响质量的情况下无法使热量加速通过塑料，*可行的方法即实现最短的冷却时间以保证冷却系统能够将热量以所需的速度从模具带走；若不可行，那么冷却系统本身就变成了热量的瓶颈，周期就会很长。如果追求最短的冷却时间，那么模塑件的壁越薄，冷却系统的效率就需要越高。不能实现最短冷却时间的原因之一是因为部件复杂，很难设置冷却通道；其它的原因可能是与设计的冷却系统不相匹配，或者在冷却通道集结了腐蚀物和水垢。为防止扭曲变形，模塑件须冷却并变得足够坚硬后方可从模具中脱出。当顶杆不再引起*性变形或者不可接受应力时，即达到时间要求。在脱模过程中发生的任何应力或者变形将取决于部件的几何形状、顶出方式、收缩率以及部件与模具之间的磨擦。在允许变形和应力的前提下决定*时间对部件进行脱模非常复杂且不切实际。相反，脱模温度——无定形材料的维卡温度以及从DSC测量的半晶体材料的冷却熔体温度——可选择，在这个温度时塑料会足够坚硬。此标准仅对何时能够进行安全脱模给出了一个粗略的估测。
PC/ABS合金目前发展迅速，全球产量约为85万吨/a左右，国需求量约为20万吨/a左右。世界各大公司纷纷开发推出PC/ABS合金新品种，如阻燃、玻纤增强、电镀、耐紫外线等品种，主要用于汽车工业、计算机、复印机和电子电气部件等。此外PC/PS(聚苯乙烯)合金、PC/PBT(聚对苯二甲酸乙二醇酯)合金、液晶聚酯改性PC、PBT/PC(由乙二醇、低分子量聚已内酯和对苯二甲酸共聚而成的多嵌段共聚酯)与PC共混改性、聚(1,4-环已烷二甲酸-1，4-环已烷二甲醇)酯改性PC等值得关注和研究开发。 典型应用范围: 1.汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件 2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器 3.电信，移动电话外壳，附件以及智能卡（SIM卡）： 4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道 5.家用电器，如洗衣机，吹风机，微波炉内外部件。
新闻动态：
原油走势回顾：国际原油价格周四从八个月高点回落，在OPEC+讨论推迟增产的会议召开前，该组织一些成员国产生了分歧，而且感恩节来临之际，大量多头获利了结离场。原油期货周四下跌1.6％。副领导人本周批评OPEC，称在要求成员国放慢产油活动前，应考虑成员国的经济和政治状况。
11月26日WTI原油日内走势图
OPEC主席周四表示，该组织必须保持谨慎，因内部数据表明明年年初可能出现新的石油过剩。到目前为止，根据今年早些时候一项协议所削减的产量大部分已经恢复。
渣打银行的Paul Horsnell在一份报告中写道，虽然预计OPEC+会延长现有减产措施，但最近油价的上涨会给一些不情愿减产的成员国（包括和阿联酋）提供理由。由于周四适逢感恩节假期，市场交易清淡，截止北京时间下午2点，1月交割的西德克萨斯州中质油期货下跌72美分，至每桶44.99美元；由于假期，周四的交易将于周五结算；1月交割的布伦特原油期货下跌1.7％至47.80美元。
原油走势分析：从日线结构来看，主趋势看多不变，破位后的加速阶段。不过1小时图经过连续的放量之后，开始出现局部浪形的三重高。如果把这波上涨当作一个浪形上涨的话，目前处于该浪形上涨的局部尾端，通常出现三重之后，小周期显示多头量能稍有放缓，会伴随一定的回踩修正再重新蓄势上涨。目前处于这种局部慢涨逼空，回踩不到位，每冲出一个新高位就伴随长时间整理修正，原油昨日延续走高，开盘即慢涨逼空，以时间换空间的整理蓄势，美盘时段再进一步的发力冲高至46.20高位，日图连阳突破前高点43.73后的放量延续。综合来看，原油今日短线操作思路上建议以回调做多为主。