美国杜邦 PET  815ER 物性表;

Processing

Injection Moulding

Delivery form

Pellets

Special characteristics

Heat stabilised or stable to heat

PRODUCT TEXT

Rynite® 815ER BK503 is a 15% Glass Reinforced, Toughened, Polyethylene Terephthalate Developed for Encapsulation Applications

PRODUCT INFORMATION

VALUE

TEST NORM

Resin Identification

PET-IGF15

ISO 1043

Part Marking Code

>PET-IGF15<

ISO 11469

RHEOLOGICAL PROPERTIES物理性能

VALUE

UNIT

TEST NORM

Melt volume-flow rate

22

cm3/10min

ISO 1133

Melt mass-flow rate

26

g/10min

ISO 1133

Temperature

280

°C

ISO 1133

Load

5

kg

ISO 1133

Melt mass-flow rate, Temperature

280

°C

ISO 1133

Melt mass-flow rate, Load

5

kg

ISO 1133

Moulding shrinkage, parallel

0.3

%

ISO 294-4, 2577

Moulding shrinkage, normal

1.0

%

ISO 294-4, 2577

MECHANICAL PROPERTIES机械性能

VALUE

UNIT

TEST NORM

Tensile Modulus

4300

MPa

ISO 527-1/-2

Stress at break

82

MPa

ISO 527-1/-2

Strain at break

5

%

ISO 527-1/-2

Flexural Modulus

3700

MPa

ISO 178

Flexural Strength

135

MPa

ISO 178

Charpy notched impact strength, 23°C

11

kJ/m2

ISO 179/1eA

Izod notched impact strength, 23°C

11

kJ/m2

ISO 180/1A

Poisson's ratio

0.36

-

-

THERMAL PROPERTIES热性能

VALUE

UNIT

TEST NORM

Melting temperature, 10°C/min

250

°C

ISO 11357-1/-3

Temp. of deflection under load, 1.8 MPa

210

°C

ISO 75-1/-2

RTI, electrical, 0.75mm

140

°C

UL 746B

RTI, electrical, 1.5mm

140

°C

UL 746B

RTI, electrical, 3mm

140

°C

UL 746B

RTI, impact, 0.75mm

120

°C

UL 746B

RTI, impact, 1.5mm

120

°C

UL 746B

RTI, impact, 3mm

120

°C

UL 746B

RTI, strength, 0.75mm

140

°C

UL 746B

RTI, strength, 1.5mm

140

°C

UL 746B

RTI, strength, 3mm

140

°C

UL 746B

FLAMMABILITY

VALUE

UNIT

TEST NORM

Burning Behav. at 1.5mm nom. thickn.

HB

class

IEC 60695-11-10

Thickness tested

1.5

mm

IEC 60695-11-10

UL recognition

yes

-

UL 94

Burning Behav. at thickness h

HB

class

IEC 60695-11-10

Thickness tested

0.81

mm

IEC 60695-11-10

UL recognition

yes

-

UL 94

Glow Wire Ignition Temperature, 3mm

775

°C

IEC 60695-2-13

FMVSS Class

B

-

ISO 3795 (FMVSS 302)

Burning rate, Thickness 1 mm

<80

mm/min

ISO 3795 (FMVSS 302)