100AF 杜邦 POM
Delrin® 100AF
ACETAL RESIN
DuPont Transportation & Industrial
Product Description:
20% PTFE Fiber Filled High Viscosity Acetal Homopolymer with Low Wear and Low Friction
| General | |
Material Status |
|
Literature 1 |
|
UL Yellow Card 2 |
|
Search for UL Yellow Card |
|
Availability | Africa & Middle EastAsia PacificEuropeLatin AmericaNorth America |
Filler / Reinforcement |
|
Additive | LubricantMold Release |
Features | High ViscosityLow FrictionWear Resistant |
RoHS Compliance |
|
Forms |
|
Processing Method | ExtrusionInjection MoldingSheet Extrusion |
Multi-Point Data | Isothermal Stress vs. Strain (ISO 11403-1)Secant Modulus vs. Strain (ISO 11403-1)Shear Stress vs. Shear Rate (ISO 11403-1)Specific Volume vs Temperature (ISO 11403-2)Viscosity vs. Shear Rate (ISO 11403-2) |
Part Marking Code (ISO 11469) |
|
Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
Density | 1.54 | g/cm3 | ISO 1183 |
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow | 1.5 | % | |
Flow | 2.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 2700 | MPa | ISO 527-2 |
Tensile Stress (Break) | 53.0 | MPa | ISO 527-2 |
Tensile Strain (Break) | 15 | % | ISO 527-2 |
Flexural Modulus | 2500 | MPa | ISO 178 |
Poisson's Ratio | 0.38 | ||
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m2 | ISO 179/1eA |
Charpy Unnotched Impact Strength (23°C) | 70 | kJ/m2 | ISO 179/1eU |
Notched Izod Impact Strength (23°C) | 5.0 | kJ/m2 | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature (1.8 MPa, Unannealed) | 87.0 | °C | ISO 75-2/A |
Melting Temperature 3 | 178 | °C | ISO 11357-3 |
CLTE | ISO 11359-2 | ||
Flow | 1.1E-4 | cm/cm/°C | |
Transverse | 1.1E-4 | cm/cm/°C | |
Annealing Temperature | 160 | °C | |
Annealing Time - Optional | 30.0 | min/mm |
| Flammability | Nominal Value | Unit | Test Method |
Burning Rate 4 (1.00 mm) | < 80 | mm/min | ISO 3795 |
Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
1.5 mm | HB | ||
3.0 mm | HB | ||
FMVSS Flammability | B | FMVSS 302 |