Product Description:
Eastman Tritan™ copolyester TX1501HF is a high flow grade of Eastman Tritan™. Eastman Tritan™ copolyester TX1501HF has viscosity reductions of 40-50% relative to Eastman Tritan™ copolyester TX1001. Eastman Tritan™ copolyester TX1501HF contains a mold release derived from vegetable based sources. Other outstanding features include good toughness, hydrolytic stability, and heat and chemical resistance. Eastman Tritan™ copolyester TX1501HF may be used in repeated use food contact articles under United States Food and Drug Administration (FDA) regulations. Eastman Tritan™ copolyester TX1501HF is certified to NSF/ANSI Standard 51 for Food Equipment Materials and is also certified to NSF/ANSI Standard 61 - Drinking Water System Components-Health Effects.
用途 | 电器用具家用货品消费品应用领域 |
机构评级 | FDA 食品接触, 未评级NSF 51NSF 61 |
加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
密度 / 比重 | 1.18 | g/cm3 | ASTM D792 |
收缩率 - 流动 | 0.50 到 0.70 | % | ASTM D955 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
洛氏硬度 (R 级, 23°C) | 111 | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 | |||
23°C | 1580 | MPa | ASTM D638 |
23°C | 1600 | MPa | ISO 527-2 |
抗张强度 | |||
屈服, 23°C | 43.0 | MPa | ASTM D638 |
屈服, 23°C | 44.0 | MPa | ISO 527-2 |
断裂, 23°C | 52.0 | MPa | ASTM D638 |
断裂, 23°C | 49.0 | MPa | ISO 527-2 |
伸长率 | |||
屈服, 23°C | 7.0 | % | ASTM D638, ISO 527-2 |
断裂, 23°C | 210 | % | ASTM D638 |
断裂, 23°C | 150 | % | ISO 527-2 |
弯曲模量 | |||
23°C | 1580 | MPa | ASTM D790 |
23°C | 1500 | MPa | ISO 178 |
弯曲应力 | |||
23°C | 60.0 | MPa | ISO 178 |
屈服, 23°C | 64.0 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
悬壁梁缺口冲击强度 | |||
23°C | 860 | J/m | ASTM D256 |
-40°C | 11 | kJ/m2 | ISO 180 |
23°C | 83 | kJ/m2 | ISO 180 |
无缺口悬臂梁冲击 (23°C) | 无断裂 | ASTM D4812 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
载荷下热变形温度 | ASTM D648 | ||
0.45 MPa, 未退火 | 94.0 | °C | |
1.8 MPa, 未退火 | 81.0 | °C |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
透射率 (总计) | 91.0 | % | ASTM D1003 |
雾度 | < 1.00 | % | ASTM D1003 |
| 注射 | 额定值 | 单位制 | |
干燥温度 | 88 | °C | |
干燥时间 | 4.0 到 6.0 | hr | |
加工（熔体）温度 | 260 到 282 | °C | |
模具温度 | 38 到 66 | °C |