| 品牌 | 美国杜邦 |
| 货号 | FG311DP |
| 用途 | 注塑级 |
| 牌号 | FG311DP |
| 型号 | FG311DP |
| 品名 | POM |
| 外形尺寸 | 颗粒 |
| 生产企业 | 美国杜邦 |
| 是否进口 | 是 |
FDA食品级 FG311DP价格优异
Features | Food Contact AcceptableHomopolymerMedium-high ViscosityNucleated |
Uses |
|
RoHS Compliance |
|
Forms |
|
Processing Method | ExtrusionFilm ExtrusionInjection MoldingSheet Extrusion |
Multi-Point Data | Isothermal Stress vs. Strain (ISO 11403-1)Secant Modulus vs. Strain (ISO 11403-1) |
Part Marking Code (ISO 11469) |
|
Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
Density | 1.42 | g/cm3 | ISO 1183 |
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 6.0 | cm3/10min | ISO 1133 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow | 1.8 | % | |
Flow | 1.9 | % | |
Water Absorption | ISO 62 | ||
Saturation, 23°C, 2.00 mm | 0.90 | % | |
Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 3300 | MPa | ISO 527-2 |
Tensile Stress (Yield) | 74.0 | MPa | ISO 527-2 |
Tensile Strain (Yield) | 15 | % | ISO 527-2 |
Nominal Tensile Strain at Break | 35 | % | ISO 527-2 |
Flexural Modulus | 3100 | MPa | ISO 178 |
Flexural Stress (3.5% Strain) | 86.0 | MPa | ISO 178 |
Poisson's Ratio | 0.37 | ||
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179/1eA | ||
-30°C | 8.0 | kJ/m2 | |
23°C | 9.0 | kJ/m2 | |
Charpy Unnotched Impact Strength | ISO 179/1eU | ||
-30°C | 250 | kJ/m2 | |
23°C | 300 | kJ/m2 | |
Notched Izod Impact Strength | ISO 180/1A | ||
-40°C | 8.0 | kJ/m2 | |
23°C | 10 | kJ/m2 |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 165 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 103 | °C | ISO 75-2/A |
Vicat Softening Temperature | 160 | °C | ISO 306/B50 |
Melting Temperature 3 | 178 | °C | ISO 11357-3 |
CLTE | ISO 11359-2 | ||
Flow | 1.1E-4 | cm/cm/°C | |
Transverse | 1.1E-4 | cm/cm/°C | |
Annealing Temperature | 160 | °C | |
Annealing Time - Optional | 30.0 | min/mm |
| Flammability | Nominal Value | Test Method | |
Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
0.75 mm | HB | ||
1.5 mm | HB |
| Additional Information | Nominal Value | Unit | Test Method |
Emission | < 8.00 | mg/kg | VDA 275 |
Fogging - G-value (condensate) | 0.40 | mg | ISO 6452 |
| Injection | Nominal Value | Unit | |
Drying Temperature | 80 | °C | |
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
Suggested Max Moisture | 0.20 | % |